Product Details:
|
| Product Name: | Mosi2 Heater | Condition: | New |
|---|---|---|---|
| Material: | MoSi2 | Shape: | U |
| Diameter: | 6/12 | Working Temperature: | 1200-1750℃ |
| Application: | Laboratory Furnaces | Voltage: | 120 Volt |
| High Light: | Mosi2 120 Volt Heating Element,Mosi2 120V Heating Element,Mosi2 Laboratory Furnace Heating Element |
||
Mosi2 Heating Element For Laboratory Furnaces
6/12 Mosi2 Heater Introduction
6/12 Mosi2 Heater is our main product. As a professional manufacturer of ceramic products, Mission has been working in this field for 5 years. Thanks to the support of our exalted customers and laborious employee. Our enterprise is developing fast. It’s our duty to provide high quality products and good service to our customers.
6/12 Mosi2 Heater Specifications
1. 1700C and 1800C heating elements.
2. U, W, UL, WL all shapes can be made
3. Very fast delivery and very competitive price
6/12 Mosi2 Heater Chemistry Character
It will form the SiO2 film which can keep the element from being melted. During the oxidizing process, the SiO2 protecting film is formed again when the element continues to be used. The MoSi2 heating element must not be used in the temperature between 400C and 700C for a long time, otherwise the element will be cremated under the strong oxidizing function in the low temperature.
Examples:
U-Shape, Material Grade 1800, D1=3mm, D2=6mm, Le=140mm, Lu=125mm, A=25mm
Specify as: MS18U, 3/6 x 140 x 125 x 25
Product Parameters:
| Physical properties | ||||
| Volume Density | Bend Strength | Porosity Rate | Water Absorption | Hot Extensiblity |
| 5.5-5.6g/cm³ | 15-25kg/ cm2 | 7.4% | 1.2% | 4% |
Oxygen-resistance under high temperature: in oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of element owing to the high temperature combustion, which prevent Mosi2 from oxidizing more. When the element temperature is higher than 1700 °C, the film becomes melting. It’s not suitable for long time use in the temperature range of 400-700°C, otherwise, the element will be powdering for the strong oxidation under low temperature.
| Atmosphere | Max. element temperature | |
| MS1700 | MS1800 | |
| Air | 1700℃ | 1800℃ |
| Nitrogen | 1600℃ | 1700℃ |
| Argon, Helium | 1600℃ | 1700℃ |
| Hydrogen | 1100-1450℃ | 1100-1450℃ |
| N2/H2 95/5% | 1250-1600℃ | 1250-1600℃ |
| Applications |
Heat treatment Forging Sintering Glass melting Refining Radiant tubes |
Laboratory furnaces Testing equipment High temperature sintering production furnaces |