Product Details:
|
Product Name: | Mosi2 Heating Rod | Feature: | High Purity |
---|---|---|---|
Material: | MoSi2 | Shape: | U, W, I, UL, WL, Spiral |
Diameter: | 9/18 12/24mm | Working Temperature: | 1200-1750℃ |
Application: | Electric Heating For Box Furnaces, Tube Furnaces, Ceramic And Etc. | After-sales Service: | Online Support |
High Light: | Mosi2 High Temperature Ceramic Heating Element,High Purity Mosi2 Element,High Purity Mosi2 Heater |
High Purity MoSi2 High Temperature Heating Element 1800℃
Mosi2 Heating Rod Advantage
1 High purity
2 High temperature resistance
3 Energy-saving
4 Chemical stability
5 Long life
6 Easy maintenance
7 Easy installation
8 Oxygen-resistance under high temperature
9 With a small expansion coefficient not easily deformed
Following should be provided when ordering Mosi2 Heating Rod
Examples:
U-Shape, Material Grade 1800, D1=3mm, D2=6mm, Le=140mm, Lu=125mm, A=25mm
Specify as: MS18U, 3/6 x 140 x 125 x 25
Product Parameters:
Physical properties | ||||
Volume Density | Bend Strength | Porosity Rate | Water Absorption | Hot Extensiblity |
5.5-5.6g/cm³ | 15-25kg/ cm2 | 7.4% | 1.2% | 4% |
Oxygen-resistance under high temperature: in oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of element owing to the high temperature combustion, which prevent Mosi2 from oxidizing more. When the element temperature is higher than 1700 °C, the film becomes melting. It’s not suitable for long time use in the temperature range of 400-700°C, otherwise, the element will be powdering for the strong oxidation under low temperature.
Atmosphere | Max. element temperature | |
MS1700 | MS1800 | |
Air | 1700℃ | 1800℃ |
Nitrogen | 1600℃ | 1700℃ |
Argon, Helium | 1600℃ | 1700℃ |
Hydrogen | 1100-1450℃ | 1100-1450℃ |
N2/H2 95/5% | 1250-1600℃ | 1250-1600℃ |