Product Details:
|
| Keywords: | 1800 MoSi2 Heating Element, Denture Furnace Heating Element, Molybdenum Disilicide Heating Element | Condition: | 1800 Type New Process |
|---|---|---|---|
| Material: | MoSi2 | Shape: | U Type |
| Diameter: | 6/12mm | Working Temperature: | 1200-1850℃ |
| Application: | Denture Furnace, Metallurgical Glass Furnace, Vacuum Furnace, Muffle Furnace, Phosphor Sintering Furnace And Other High-temperature Electric Furnaces | After-sales Service: | Online Support |
| High Light: | MoSi2 Furnace Heating Element Replacement,9/18mm Furnace Heating Element Replacement,U Furnace Heating Element Replacement |
||
6 / 12mm 1800 type MoSi2 heating element, denture furnace heating element
Furnace Heating Element Replacement Advantage:
A. It has anti-oxidation
B. function and can be used continually in oxidative atmosphere.
C. We are using thermal processing in shape,which maintains a very good high-temperature tenacity and plasticity of the basic materials.
D. the cold and hot end welding aspect, it uses special joint technology to take shape.
E. The product has high density that greatly improves the conductivity of the product.
When you place order, please tell us following data:
d = the diameter of hot zone
c = the diameter of cold zone
Le = the length of hot zone
Lu = the length of cold zone
A = the distance between two terminals
Examples:
U-Shape, Material Grade 1800, D1=3mm, D2=6mm, Le=140mm, Lu=125mm, A=25mm
Specify as: MS18U, 3/6 x 140 x 125 x 25
Product Parameters:
| Physical properties | ||||
| Volume Density | Bend Strength | Porosity Rate | Water Absorption | Hot Extensiblity |
| 5.5-5.6g/cm³ | 15-25kg/ cm2 | 7.4% | 1.2% | 4% |
Oxygen-resistance under high temperature: in oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of element owing to the high temperature combustion, which prevent Mosi2 from oxidizing more. When the element temperature is higher than 1700 °C, the film becomes melting. It’s not suitable for long time use in the temperature range of 400-700°C, otherwise, the element will be powdering for the strong oxidation under low temperature.
| Atmosphere | Max. element temperature | |
| MS1700 | MS1800 | |
| Air | 1700℃ | 1800℃ |
| Nitrogen | 1600℃ | 1700℃ |
| Argon, Helium | 1600℃ | 1700℃ |
| Hydrogen | 1100-1450℃ | 1100-1450℃ |
| N2/H2 95/5% | 1250-1600℃ | 1250-1600℃ |
| Applications |
Heat treatment Forging Sintering Glass melting Refining Radiant tubes |
Laboratory furnaces Testing equipment High temperature sintering production furnaces |