| Product Name: | Mosi2 Heater | Condition: | New Process |
|---|---|---|---|
| Material: | MoSi2 | Shape: | L Type |
| Diameter: | 3/6, 4/9, 6/12, 9/18, 12/24mm | Working Temperature: | 1200-1750℃ |
| Application: | High Temperature Electric Furnaces | After-sales Service: | Online Support |
| High Light: | L Type Mosi2 Heater,Mosi2 Heater 1800 Degree,Electric Furnaces Mosi2 Heater |
||
L Type Mosi2 Heater 1800 Degree High Temperature Electric Furnaces
Following should be provided when ordering U Type MoSi2 Heating Elements:
Examples:
U-Shape, Material Grade 1800, D1=3mm, D2=6mm, Le=140mm, Lu=125mm, A=25mm
Specify as: MS18U, 3/6 x 140 x 125 x 25
Product Parameters:
| Physical properties | ||||
| Volume Density | Bend Strength | Porosity Rate | Water Absorption | Hot Extensiblity |
| 5.5-5.6g/cm³ | 15-25kg/ cm2 | 7.4% | 1.2% | 4% |
Oxygen-resistance under high temperature: in oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of element owing to the high temperature combustion, which prevent Mosi2 from oxidizing more. When the element temperature is higher than 1700 °C, the film becomes melting. It’s not suitable for long time use in the temperature range of 400-700°C, otherwise, the element will be powdering for the strong oxidation under low temperature.
| Atmosphere | Max. element temperature | |
| MS1700 | MS1800 | |
| Air | 1700℃ | 1800℃ |
| Nitrogen | 1600℃ | 1700℃ |
| Argon, Helium | 1600℃ | 1700℃ |
| Hydrogen | 1100-1450℃ | 1100-1450℃ |
| N2/H2 95/5% | 1250-1600℃ | 1250-1600℃ |
| Applications |
Heat treatment Forging Sintering Glass melting Refining Radiant tubes |
Laboratory furnaces Testing equipment High temperature sintering production furnaces |