Product Details:
|
| Product Name: | Molybdenum Disilicide Heating Element | Feature: | High Purity |
|---|---|---|---|
| Material: | MoSi2 | Shape: | U, W, I, UL, WL, Spiral Shape |
| Diameter: | 9/18mm Diameter | Working Temperature: | 1200-1750℃ |
| Application: | Box Furnaces, Tube Furnaces, Ceramic And Etc. | After-sales Service: | Online Support |
| High Light: | 1750C Molybdenum Disilicide Heating Element,18mm Molybdenum Disilicide Heating Element,9/18mm Molybdenum Disilicide Heating Element |
||
1750C Molybdenum Disilicide Heating Element 9/18mm Diameter
MoSi2 Heating Element Advantage
1 High purity
2 High temperature resistance
3 Energy-saving
Following should be provided when ordering Mosi2 Heating Rod
Examples:
U-Shape, Material Grade 1800, D1=3mm, D2=6mm, Le=140mm, Lu=125mm, A=25mm
Specify as: MS18U, 3/6 x 140 x 125 x 25
Product Parameters:
| Physical properties | ||||
| Volume Density | Bend Strength | Porosity Rate | Water Absorption | Hot Extensiblity |
| 5.5-5.6g/cm³ | 15-25kg/ cm2 | 7.4% | 1.2% | 4% |
Oxygen-resistance under high temperature: in oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of element owing to the high temperature combustion, which prevent Mosi2 from oxidizing more. When the element temperature is higher than 1700 °C, the film becomes melting. It’s not suitable for long time use in the temperature range of 400-700°C, otherwise, the element will be powdering for the strong oxidation under low temperature.
| Atmosphere | Max. element temperature | |
| MS1700 | MS1800 | |
| Air | 1700℃ | 1800℃ |
| Nitrogen | 1600℃ | 1700℃ |
| Argon, Helium | 1600℃ | 1700℃ |
| Hydrogen | 1100-1450℃ | 1100-1450℃ |
| N2/H2 95/5% | 1250-1600℃ | 1250-1600℃ |