Product Details:
|
Name: | Mosi2 Heater | Function: | Electric Heating |
---|---|---|---|
Material: | MoSi2 Material | Shape: | U Shape |
Diameter: | 3/6, 4/9, 6/12, 9/18, 12/24mm | Working Temperature: | 1700/1800 |
Application: | This High Temperature Kiln | After-sales Service: | Online Support |
High Light: | 1800 U Shape Mosi2 Heater,Mosi2 moly disilicide heating elements,Mosi2 molybdenum disilicide heater |
1700/1800 Mosi2 Heater For Various Electric Furnaces
Mosi2 Heater Feature
1. Mosi2 Heater for various electric furnaces.
2. Long life combined with ease of replacing failed elements
3. Can be used continuously or intermittently
4. New and old elements can be connected in series
5. High power concentration may be applied
Following should be provided when ordering MoSi2 Heating Element :
Examples:
U-Shape, Material Grade 1800, D1=3mm, D2=6mm, Le=140mm, Lu=125mm, A=25mm
Specify as: MS18U, 3/6 x 140 x 125 x 25
MoSi2 Heating Element Parameters:
Physical properties | ||||
Volume Density | Bend Strength | Porosity Rate | Water Absorption | Hot Extensiblity |
5.5-5.6g/cm³ | 15-25kg/ cm2 | 7.4% | 1.2% | 4% |
Oxygen-resistance under high temperature: in oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of element owing to the high temperature combustion, which prevent Mosi2 from oxidizing more. When the element temperature is higher than 1700 °C, the film becomes melting. It’s not suitable for long time use in the temperature range of 400-700°C, otherwise, the element will be powdering for the strong oxidation under low temperature.
Atmosphere | Max. element temperature | |
MS1700 | MS1800 | |
Air | 1700℃ | 1800℃ |
Nitrogen | 1600℃ | 1700℃ |
Argon, Helium | 1600℃ | 1700℃ |
Hydrogen | 1100-1450℃ | 1100-1450℃ |
N2/H2 95/5% | 1250-1600℃ | 1250-1600℃ |