Product Details:
|
| Product Name: | High Temperature Silicon Carbide Heating（SiC） Element For Furnace | Density: | 2.8g/Cm³ |
|---|---|---|---|
| Shape: | ED/U/W/SC/SCR/DB/G/H/DM | Application: | Electric Furnaces |
| Power Source:: | Electric Power | Working Temperature:: | Up To 1450℃ |
| High Light: | SiC Silicon Carbide Heating Element,High Temperature Silicon Carbide Heating Element,Silicon Carbide Heating Element For Furnace |
||
High temperature silicon carbide heating(SiC) element for furnace
Product Description
Silicon Carbide Heating Elements is a kind of non-metal high temperature electric heating element. . In oxidizing atmosphere, its service temperature can reach 1450ºC and continuous use life can reach 2000 hours.It can usually make use for furnance which temperature from 600C-1600ºC. It is widely used in various electric heating element of glass,chemical, electronic material and so on.Silicon carbide electric heating elements are full of varieties, high quality, low price, and products are sold all over the world.
Product pictures
Advantages:
| 1 | Withstands high temperature up to 1600℃ |
| 2 | High strength and excellent shock resistance |
| 3 | Heat source without noise and air pollution |
| 4 | Anti-oxidation, anti-corrosion,small deformation, long life |
| 5 | Various shapes:ED/U/W/SC/SCR/DB/G/H/DMshapes are availible |
| 6 | Convenient installation and maintenance |
Recommended surface load and Influences to Surfaces of the Elements in Different Operating Temperature
| atmosphere | Furnace Temperature(°C) | Surface Load(W/cm2) | The influence on the Rod |
| Ammonia | 1290 | 3.8 | The action on SiC produces methane and destroys the protection film of SiO2 |
| Carbon dioxide | 1450 | 3.1 | Corrode SiC |
| Carbon monoxide | 1370 | 3.8 | Absorb carbon powder and influence the protection film of SiO2 |
| Halogen | 704 | 3.8 | Corrode SiC and destroy the protection film of SiO2 |
| Hydrogen | 1290 | 3.1 | The action on SiC produces methane and destroys the protection film of SiO2 |
| Nitrogen | 1370 | 3.1 | The action on SiC produces insulating layer of silicon nitride |
| Sodium | 1310 | 3.8 | Corrode SiC |
| silicon dioxide | 1310 | 3.8 | Corrode SiC |
| Oxygen | 1310 | 3.8 | SiC oxidized |
| Water-vapor | 1090-1370 | 3.1-3.6 | The action on SiC produces hydrate of silicon |
| Hydrocarbon | 1370 | 3.1 | Absorb carbon powder resulted in Hot pollution |
Packing & Delivery
Installation and Operation
1. In order to keep the furnace temperature and the charges uniform of each element, resistance values must be matched first before installation, arrange those with close current values on the same circuit.
2. As the heating elements are made of ceramic, avoid damage from mechanical shock.
3. The diameter of a piercing hole drilled through the furnace should be about 1.5 times the diameter of the element's end section. Size under 20mm is suitable for bricklayers up to 150mm in thickness. Size under 25mm is suitable for bricklayers up to 250mm in thickness.